 | FILLERS | |
BLR 2
A very fine, white calcium carbonate powder, It is mixed in polyester resins in casting and for RTM Light resins giving lower exotherm and less shrinkage.
CAB-O-SIL
Untreated fumed silica. Used for rheology control |
|
CHROMOS
VINYLESTER FOR HIGH STRENGTH AND CHEMICAL PROPERTIES |
Epoxi vinylester resin.
Outstanding resistance to corrosion in acids and alkalis at room temperatures. Suitable for fabrication of fibre reinforced composites by conventional techniques. |
Chromovinyl V-276
Chromovinyl V-271 lower viscosity version | HDT 90-95 degree C
HDT 100-105 degree C |
| | |
Epoxi novalac vinylester resin.
Corrosion resistance properties as V-271 and V276, however better chemical resistance to chlorinated solvents, superior oxidation resistance and resistance to mixture of chemicals including solvents. Higher HDT. Superior retention of properties at higher temperatures |
| Chromovinyl V273 | HDT 120 degree C |
DIVINYCELL INTERNATIONAL AB PVC Foam, Balsa
Sandwich material for optimal high strength-to-weight ratio. |
|
AKZO NOBEL Peroxides
* Butanox M50 Standard general purpose catalyst. MEKP. Suitable for gelcoats/marine applications
* Butanox LPT Longer geltime and suitable for large mouldings. Very suitable for Filament Winding
* Trigonox 44B Comparable geltime with M50 but faster cure. Suitable for general moulding RTM
* Other qualities available with longer delivery times. |
|
SCOTT BADER ACCELERATOR RANGE
* Accelerator G A solution of cobalt in styrene (1% Cobalt)
* Accelerator E A solution of cobalt in styrene (0,4% Cobalt)
* Accelerator R A solution of cobalt in styrene (6% Cobalt)
* Accelerator D Amine accelerator for use with resins in conjunction with benzoyl peroxide
catalysts (10%DMA) |
|
|
MATLINE+ (Chomarat Composites)
A chemically non-woven material impregnated with micro spheres and expanded to a thickness of 1mm – 5 mm. It is a fully mouldable core material and is compatible with most resin systems to produce lightweight sandwich panels.
New Improved quality offering: Better dry drapability, Reduced resin consumption, Better adherence on vertical applications
Available thickness; 1mm, 2 mm, 3 mm, 4 mm and 5 mm
a |
| Product Reference: | Matline 100+
Matline 200+
Matline 300
Matline 400+
Matline 500+ | |
|
EPOXI
WEST SYSTEM Epoxy
Laminating clear, light amber, low viscosity resin designed specially for use within the marine industry for construction, repair and maintenance.
Resin 105
Hardeners 205 Standard
206 Slow
Different Fillers, Micro fibres and additives available for bonding, fairing and coating.
|
|
CLEANING MATERIALS, PROTECTIVE EQUIPMENT AND BOOKS
Acetone
200 lit barrels
Hand Cream
Clean All Paste and liquid easily removes uncured resin from skin
Crystic Polyester Handbook |
|
| ALUMINIUM ROLLERS | |
| 
(Items no with * are stock items others on order)
| Art. Nr: Pack: Length Diameter:
1722: Paddle Roller 10pcs 140mm 45mm
1721: Paddle Roller 10pcs 70mm 45mm
1725: Paddle Roller 10Pcs 140mm 21mm
1720: Paddle Roller 10pcs 70mm 21mm
1728: Corner Roller 5pcs 11mm 40mm (L:300mm)
1729: Corner Roller 5pcs 11mm 40mm (L:500mm)
1732: Fine Roller 10Pcs 70mm 30mm
1731: Fine Roller 10Pcs 140mm 22mm
1724: Fine Roller 10pcs 35mm 12mm
1727: Fine Roller 10pcs 70mm 12mm
1726: Bristle Roller 10pcs 100mm, 30mm
2300: Dosimeter,1liter 1pcs |
| All rolls are made in a strong cast steel (nickel-platted) ,with ergonomic plastic grip control. All of the rolls can be provided with telescopic extensions |
|
 | Farecla G3 Polishing compound
Finishing Pad, Compounding Pad, Backing Plate (14mm threaded) |  |
|
 | HAND CLEANER Kleen All Paste hand cleanser, for the safe fast removal of all paints, unsolved resins, adhesive, grease, etc. Rinse thoroughly with water to leave |
1800: Kleen All Past Hand Cleanser 12pcs/kart
1800: Kleen All Past Hand Cleanser 1pcs | |
|
 | | PRODUCT SPECIFICATION |
|
TR 100 & 200
TR 102 Regular
Fast application, excellent breakdown, high production wax that can be allowed to sit during breaks due to its easy removal characteristic. Our most popular solid paste wax.
TR 104 Hi-Temp Wax
Often referred to as Blue wax, it is ideal for thicker laminates, is easily applied, and gives reduced build up due to the carnauba base.
TR 210 Self-Stripping Liquid Mold Release
A high production liquid mould release formulated to eliminate wax build up problems in the Cultured Marble and Fiberglas Reinforced Plastics Industries. It produces lustrous high gloss finish and sure positive releases. Reduced mold prep time, elimination of wax build up and extended mould life are ways TR 210 liquid release improves efficiency. Liquid mold release is recommended for use on fully cured, well conditioned moulds only.
TR 216 Regular Liquid Mould Release
Liquid version of TR 104 | A | TR 900 Semi-permanents
TR 905 Solvent Mould Prep Cleaner
A proprietary solvent mixture to remove wax, oils and other surface contaminates from reinforced polyester tooling and other hard surface moulds. Recommended for preparation and cleaning of mould surface prior to application of TR-920 Semi-Permanent RELEASE or the TR-910 SEALER.
TR 910 Liquid Semi-Permanent Sealer
TR-910 SEALER is a resilient moisture cure film-forming base coat which acts to seal the mould surface before application of the TR-900 series semi-permanent release agents.
* Protects against STYRENE attack and maximises performance of the Liquid Semi-Permanent Release agents
* Aids break-in release and seals porosity.
TR 920
TR-920 is a high-temp multiple capability semi-permanent release coating which cures under atmospheric conditions, bonding a durable thin clear release on the mould. Gives multiple releases for polyester, epoxy applications.
* Excellent hi-temp properties.
* Multiple releases per application.
* Easily recoats without build-up or transfer. |
|
|